|Materials||PPMgOCLN, Doping: 5mol% bulk||Aperture Size||2.2(±0.1) x 0.5 (±0.05)mm|
|Flatness||< Lambda/8 @ 633nm||Wavefront Distortion||< Lambda/6 @ 633nm|
|Chips||<0.1mm||Surface Quality||20/10 S/D|
|Coating||AR coating||Applications||SHG 1064nm|
Chemical and Optical Properties:
|Melting Point||1255+/-5℃||Curie Point/Temperature||1140+/-5℃|
|Thermal Conductivity||38W/m/K @ 25℃||Coefficient of Thermal Expansion||
|Wavelength Range of Transmission||420nm ~ 5200nm||Nonlinear Coefficient||
d33 = 34.4 pm/V
d31 = d15 = 5.95 pm/V
d22 = 3.07 pm/V
|Optical Damaging Threshold||0.3GW/cm2||Absorptive Coefficient||0.004/cm @ 1064nm|
PPLN Crystals for SHG 1064nm, 2.2x0.5x25mm Code: 2091-013
Periodically poled lithium niobate (PPLN) crystals are a type of highly efficient non-linear optical crystal, which cover an extremely wide wavelength conversion spectral range of 0.4μm to 5.0μm, and is a crucial component for fabricating integrated PPLN Waveguide Modules. The 5% MgO doping in LiNbO3 would increase the optical resistance of the crystals and significantly improve its damage threshold. MgO: PPLN could be used for Second Harmonic Generation (SHG), Optical Parametric Oscillator (OPO), Optical Parametric Amplifier (OPA), Sum Frequency Generation (SFG) and Difference Frequency Generation (DFG). By choosing the proper period, width, and length, one can obtain the required specific frequency conversion.
Hangzhou Shalom EO offers a series of MgO:PPLN crystals for SHG of 976nm, 1029nm,1064nm, 1545nm, 1550nm, 1560nm, and 2100nm, PPLN crystals for SFG, DFG, and OPO applications are also available.